4Cr13 420 S136 1.2083 Stainless Steel Sheet High Strength With Heat Treatment
Similar Standards
| Chinese | American | German | Swedish | Japanese | Japanese |
| GB | AISI | DIN | ASSAB | JIS | DAIDO |
| 4Cr13 | 420 | 1.2083 | S136 | SUS420J2 | S-STAR |
Chemical Composition
| Grades | C | Si | Mn | P | Mo | Ni | V | Cr |
| 1.2083 | 0.38-0.45 | ≤1.0 | ≤1.0 | ≤0.03 | / | 2.5-3.5 | / | 12.0-13.5 |
| 420 | 0.16-0.25 | ≤1.0 | ≤1.0 | ≤0.04 | / | ≤0.75 | / | 12.0-14.0 |
| 4Cr13 | 0.36-0.45 | ≤0.6 | ≤0.8 | ≤0.035 | / | ≤0.6 | / | 12.0-14.0 |
| S136 | 0.34-0.42 | 0.6-1.3 | / | ≤0.030 | 0.30-0.55 | 0.15-0.40 | 13.0-14.5 |
Heat Treatment
| Quenching | Tempering | ||||
| Heating Temperature/ºC | Cooling | Hardness/HRC | Heating Temperature/ºC | Cooling | Hardness/HRC |
| 1000-1050 | Oil | 52-55 | 200-300 | Air | 50-53 |
Mechanical properties editing
● Mechanical properties: Hardness: Annealing, ≤201HB, indentation diameter 3.9 ～ 4.3mm; quenching, ≥50HRC
● Heat treatment specifications and metallographic structure:
Heat treatment specifications:
1) Annealing, slow cooling at 800 ～ 900 ℃ or quick cooling at about 750 ℃;
2) Quenching, oil cooling at 1050 ～ 1100 ℃
3) Tempering, quick cooling at 200 ～ 300 ℃.
Metallographic structure: The structure is characterized by martensite.